Zhengzhou Fangming High Temperature Ceramic New Material Co., Ltd.
Zhengzhou Fangming High Temperature Ceramic New Material Co., Ltd.
Add to Cart
95% 96% ZrO2 Zirconia Nozzle Flow Control Refractory Low Density
Zirconia Nozzle Introduction
The Zirconia Nozzle are manufactured without the use of cement jointing, using an insert and pressed outer body. This method of manufacture provides a reliable system with no risk of steel leakage between the insert and outer body.
Inspection times in the production process
1. After Mixing, inspect the water content of material,
2. After pressing, inspect the size,missing angle, etc. of semi-finished products
3. After sintering, inspect the size, missing angle, cave, etc. of finished products
4. Before packing, inspect the size, missing angle, cave,of the finished prodcuts again.
Chemical Composition of Zirconia Nozzle
| Model | Chemical Composition | Physical Properties | ||||
|
ZrO2 (%) |
Al2O3 (%) |
SiO2 (%) |
MgO (%) |
Bulk Density (g/cm3) |
Apparent Porosity (%) | |
| FMXC-ZN-007 | 95-96 | ---- | ---- | 2.7-2.9 | 5.1-5.15 |
5-7 |
Size Tolerance:
Middle Hole Diamter:+-0.2mm, other sizes: +-1mm.
Exported Countries
India, Pakistan, Iran, Thailand, Turkey, Peru, USA, etc.
Fangming NewM's Goal
Large size, super special shaped super high temp. zirconia ceramics, we will offer the comprehensive and integrated super high temperature, strong crushing resistance, strong erosion resistance application condition solutions.